What would happen to the physical properties of a cold worked material if it were fully annealed and cold worked further?

It would have approximately the same characteristics of the material before it was annealed.

In other Words, it would almost be the same as the first time it was cold worked, assuming nothing was done to the material before it was cold worked the first time.